Preparation and characterization of electrolytic alumina deposit on austenitic stainless steel

Conversion coating modified by alumina has been studied as a way for improving the resistance to thermal oxidation of an austenitic stainless steel. Conversion coating, characterized by a particular morphology and strong interfacial adhesion with the substrate, facilitate the electrochemical deposition of ceramic layers and enhance their adhesion to the substrate. The influence of the current density and treatment time on alumina deposit was studied using statistical experimental designs like Doehlert uniform shell design. After heating, coatings present a continuous composition gradient with refractory compounds at the surface. The behavior at high temperature (1000 8C) of the alumina coating was investigated. The presence of alumina increases the oxidation resistance of an austenitic stainless steel at 1000 8C. The morphology and the chemical composition of the deposit are analyzed. Results on the thermal stability of coating on austenitic stainless steel are presented

Supported TiO2 on Borosilicate Glass Plates for Efficient Photocatalytic Degradation of Fenamiphos

Supported titanium dioxide (TiO2) was investigated for the photodegradation of the insecticide fenamiphos in water. The photocatalyst was immobilised on borosilicate glass plates and the kinetics of degradation were studied in a stirred tank reactor under UV irradiation. Two types of TiO2, for example, Millennium PC500 (100% anatase) and Degussa P25 (80% anatase, 20% rutile), were used. Their activities have been based on the rates of insecticide disappearance. Experiments were investigated to evaluate the effect of pH and initial concentrations of fenamiphos as well as catalyst doses on the photocatalytic degradation of fenamiphos. Kinetic parameters were experimentally determined and an apparent first-order kinetic was observed. For photolysis process of fenamiphos, two photoproducts were identified and characterized using high performance liquid chromatography/mass spectrometry (HPLC/MS). The plausible mechanism of photolysis involved is the oxidation of sulfonamide group. In presence of photocatalyst TiO2, photodegradation was observed. Under identical conditions, Degussa P25 shows higher photocatalytic activity in regard to PC500 Millennium and complete degradation was observed after 180 min